| No. | 配信 | タイトル・著者（所属） |
|---|---|---|
| 1 | ◯ |
A study of superplasticity in Fe-Mn-(Al-Si)-C low density steels Junyeong Jeong･Jaeyoon Hwang･Minwoo kang (Hyundai Motor)･Jeongho Han (Hanyang University) Low density steel sheets can exhibit super-plasticity properties under characteristic composition and process conditions, so they can be applied to large-sized plate parts with high forming difficulty based on high elongation in a single press process, which has the advantages of process simplification (welding deletion, etc.) and mold reduction. We designed various compositions of Fe-Mn-(Al-Si)-C low-specific-weight steel sheets, evaluated super-plasticity properties, analyzed the cause of its occurrence, and verified the properties at room temperature in consideration of future part applicability |
| 2 | ◯ |
高強度鋼板部品の水素脆化割れ防止技術の開発 矢倉 聖也・常見 祐介・木本 野樹・久保 雅寛（日本製鉄） 一般に，高強度材料では水素脆化割れが課題となる場合がある．本研究では，自動車部品を想定し，せん断端面での水素脆化割れへの変形と残留応力の影響に着目した検討を行った．せん断端面での残留応力を低下させる手法を検討し，その一例として，せん断端面を圧縮することで残留応力が低下することを検証した． |
| 3 | ✕ |
水素燃焼を想定した雰囲気下におけるフェライト系ステンレス鋼の酸化挙動 藤村 佳幸・林 篤剛・平川 直樹・濱田 純一（日本製鉄） 水素燃焼を想定し，各種フェライト系ステンレス鋼について，30%H₂O–N₂雰囲気下で400～700℃×100時間の熱処理を行い，水蒸気酸化挙動を調査した．酸洗仕上材では600℃で重量増加が最大となり，高Cr，Siの鋼種ほど耐酸化性が優れた．また，低Cr，Siの鋼種であっても研磨仕上材では酸化が顕著に抑制された． |
| 4 | ◯ |
熱間鍛造駆動系浸炭部品の異常粒成長発生予測 伊藤 靖朗・加藤 豪・前田 誠（ジヤトコ）・山下 翼・和田 直樹・小島 秀平（MI-6株式会社）・井上 純哉（東京大学） 熱間鍛造を施した駆動系浸炭部品では，強度低下を引き起こす異常粒成長が発生する．その予測は複雑な発生機構であるため困難である．本研究では，熱間鍛造を模擬した試験結果を機械学習により解析し，部品製造時に制御可能な因子から異常粒成長の発生を予測する手法を開発した． |
| 5 | ◯ |
ダイカスト用溶湯難燃マグネシウム合金の開発 千野 靖正（産業技術総合研究所）・駒井 浩（日本マグネシウム協会） 日本マグネシウム協会では「自動車マグネシウム適用拡大委員会（2014～2018）」において，安全性向上と防燃ガス不要を目指し，溶解工程で燃焼し難いダイカスト用溶湯難燃性マグネシウム合金の開発を行った．本発表では開発した合金の難燃特性や機械的特性，耐食性を紹介すると共に試作した部品の特性を紹介する． |
| 6 | ◯ |
疲労限度線図と疲労寿命予測モデルについて 王 暁光（東京濾器） 疲労限度や寿命は負荷方式によって異なり，応力集中によっても大きく影響される．平均応力の影響はいくつかのモデルを用いて数学的に表現されているが，実験データに基づくと，Walkerモデルが最も適切であり，高い予測精度を有することが示された．溶接による組立応力が疲労限度に及ぼす影響や，下限界応力拡大範囲についても同様であった． |